ภาพรวม
Polycrystalline Mullite Fiber (PMF) is a novel super-light high temperature refractory fiber in the world, one of the whole Al2O3-SiO2 system ceramic fibers, with use temperature of 1800 degrees to 1700 degrees, 200 degrees to 300 degrees higher that that of fiber glass.
Polycrystalline mullite fiber (PMF) is currently at home and abroad the latest ultra-lightweight high-temperature fire resistant fiber, the whole system Al2O3SiO2 ceramic fibers in two different products, It can be widely used in metallurgy, machinery, electronics, ceramics, chemicals, aerospace and other high temperature industrial furnaces and other thermal equipment, lined with insulation.
เพื่อให้บรรลุประสิทธิภาพการใช้พลังงานเพิ่มขึ้น ยืดอายุการใช้งานเตา เพื่อปรับปรุงสภาพแวดล้อมการทํางาน มีลักษณะภายนอกสีขาว ผิวเรียบ นุ่ม ยืดหยุ่น เหมือนฝ้าย
ลักษณะ
It is characterized in white appearance, smoothness, softness and elasticity, just like pledget. PMF is a polycrystalline mullite fiber in the existing form of mullite crystalling phase, with a unique structure, complicated manufacturing process and high technical content.
- ความเสถียรที่อุณหภูมิสูง 1600-1800C
- เหมาะสําหรับใช้เป็นฉนวนเตาในกระบวนการเตรียม บําบัดความร้อน และเคมีทางความร้อน
- ไม่ติดไฟ
- ทนการเปลี่ยนแปลงอุณหภูมิอย่างรวดเร็วได้ดี
- ต้านทานต่อการโจมตีทางเคมีได้ดี มีความเสถียรยอดเยี่ยมในกากสลากโลหะกรด และไม่ละลายในกรดส่วนใหญ่
- ต้านทานต่อการออกซิไดซ์และการกัดกร่อนจากบรรยากาศในเตา
- ต้านทานต่อการขัดสี
- มีค่าความต้านทานไฟฟ้าสูง
- ความเสถียรทางความร้อนสูง
- สามารถใช้เป็นฉนวนกั้นช่องว่างในเตาและรอบท่อลอดและช่องเปิดของเตาได้
- อุดรอยต่อขยายและรอยแตกภายในเตา
ประเภทต่างๆ
| Ceramic fiber board | SS1050C-RBD | SS1260 ST-RBD | SS1260 HP-RBD | SS1350 HA-RBD | SS1430 Zr-RBD | SS1600 PCF-RBD | SS1700 PCF-RBD | SS1800 PCF-RBD | |
| Max Service Temperature(℃) | 1050 | 1260 | 1260 | 1350 | 1430 | 1600 | 1700 | 1800 | |
| Density (kg/m³) | 220/250/280/300/320/350/380/400 | 400/450/500/550 | |||||||
| Linear hrinkage(%) (After burning)(24h) | ≤3.0 950℃ | ≤3.0 1050℃ | ≤3.0 1100℃ | ≤3.0 1200℃ | ≤3.0 1300℃ | ≤1.0 1450℃ | ≤1.0 1550℃ | ≤1.0 1650℃ | |
| (MPa)Modulus of rupture | ≥0.3 | ≥0.4 | ≥0.4 | ≥0.4 | ≥0.4 | ≥0.6 | ≥0.6 | ≥0.6 | |
| (%)Loss on ignition | ≤8.0 | ≤4.0 | |||||||
| Thermal conductivity rate(W/m.k) | 400℃ | 0.08 | – | – | – | – | – | – | – |
| 600℃ | 0.12 | 0.12 | 0.12 | 0.12 | – | – | – | – | |
| 800℃ | 0.16 | 0.16 | 0.16 | 0.16 | 0.16 | 0.17 | 0.17 | 0.17 | |
| 1000℃ | – | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | |
| Chemical Composition(%) | Al2O3 | ≥37 | ≥41 | ≥43 | ≥45 | ≥37 | ≥65 | ≥70 | ≥72 |
| Al2O3+SiO₂ | ≥97 | ≥97 | ≥98 | ≥98 | ≥84 | ≥99 | ≥99 | ≥99 | |
| ZrO₂ | – | – | – | – | ≥11 | – | – | – | |
| อื่นๆ | ≤3.0 | ≤3.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤1.0 | ≤1.0 | ≤1.0 | |
| Standard size（L*W*T）mm | 1200/600*1000*(6-105),1200*500*(6-105) | 1000/900*600*20-150 | |||||||
| Package | Cartons or Pallets | Wooden | |||||||
| Other sizes of products and packages are available as required. | |||||||||
| Recommended using temperature:In oxidizing or neutral atmosphere,100~250℃Recommended usingtemperature:In oxidizing or neutral atmosphere,100∽250℃lower than the maximum service temperature,In reductive atmosphere,200~350℃ lower than the maximum service temperature. | |||||||||
การประยุกต์ใช้งาน
- ยางกันซึมอุณหภูมิสูง
- ส่วนกันกร่อนภายในทาบางๆ
- วัสดุผิวร้อนของผนังเตาอุณหภูมิสูง
- การฉนวนความร้อนของอุปกรณ์ทําความร้อน
- วัสดุอุดประตูเตาและตัวเตา