مقدمة عامة
Polycrystalline Mullite Fiber (PMF) is a novel super-light high temperature refractory fiber in the world, one of the whole Al2O3-SiO2 system ceramic fibers, with use temperature of 1800 degrees to 1700 degrees, 200 degrees to 300 degrees higher that that of fiber glass.
Polycrystalline mullite fiber (PMF) is currently at home and abroad the latest ultra-lightweight high-temperature fire resistant fiber, the whole system Al2O3SiO2 ceramic fibers in two different products, It can be widely used in metallurgy, machinery, electronics, ceramics, chemicals, aerospace and other high temperature industrial furnaces and other thermal equipment, lined with insulation.
وذلك بهدف تحقيق زيادة كفاءة الطاقة، وتمديد عمر الفرن، وتحسين بيئة العمل. يتميز بلون أبيض، وسطح ناعم، ونعومة ومرونة، تمامًا كالقطن.
السمة
It is characterized in white appearance, smoothness, softness and elasticity, just like pledget. PMF is a polycrystalline mullite fiber in the existing form of mullite crystalling phase, with a unique structure, complicated manufacturing process and high technical content.
- استقرار درجة الحرارة العالية حتى 1600-1800 درجة مئوية
- مثالي للاستخدام كعزل الفرن في عمليات السنفرة وعلاج الحرارة وأنظمة معالجة الحرارة الكيميائية
- غير قابل للاشتعال
- مقاومة ممتازة لصدمات الحرارة
- مقاومة لمعظم الهجمات الكيميائية؛ حيث تتميز بالاستقرار الممتاز في السوائل الحمضية للمعادن ولا تذوب في معظم الأحماض
- مقاومة للأكسدة وهجمات البيئات الفرنية
- مقاومة للاهتراء
- مقاومة كهربائية جيدة
- استقرار حراري ممتاز
- يمكن استخدامه كعزل داخل مساحات الفرن وحول أنابيب الرؤية والفتحات في الفرن.
- يمكن استخدامه لملء فواصل التمدد والشقوق في الجوانب الداخلية للأفران.
أنواع مختلفة
| Ceramic fiber board | SS1050C-RBD | SS1260 ST-RBD | SS1260 HP-RBD | SS1350 HA-RBD | SS1430 Zr-RBD | SS1600 PCF-RBD | SS1700 PCF-RBD | SS1800 PCF-RBD | |
| Max Service Temperature(℃) | 1050 | 1260 | 1260 | 1350 | 1430 | 1600 | 1700 | 1800 | |
| Density (kg/m³) | 220/250/280/300/320/350/380/400 | 400/450/500/550 | |||||||
| Linear hrinkage(%) (After burning)(24h) | ≤3.0 950℃ | ≤3.0 1050℃ | ≤3.0 1100 درجة مئوية | ≤3.0 1200℃ | ≤3.0 1300 ℃ | ≤1.0 1450℃ | ≤1.0 1550℃ | ≤1.0 1650℃ | |
| (MPa)Modulus of rupture | ≥0.3 | ≥0.4 | ≥0.4 | ≥0.4 | ≥0.4 | ≥0.6 | ≥0.6 | ≥0.6 | |
| (%)Loss on ignition | ≤8.0 | ≤4.0 | |||||||
| Thermal conductivity rate(W/m.k) | 400℃ | 0.08 | – | – | – | – | – | – | – |
| 600℃ | 0.12 | 0.12 | 0.12 | 0.12 | – | – | – | – | |
| 800℃ | 0.16 | 0.16 | 0.16 | 0.16 | 0.16 | 0.17 | 0.17 | 0.17 | |
| 1000℃ | – | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | 0.23 | |
| Chemical Composition(%) | Al2O3 | ≥37 | ≥41 | ≥43 | ≥45 | ≥37 | ≥65 | ≥70 | ≥72 |
| Al2O3+SiO₂ | ≥97 | ≥97 | ≥98 | ≥98 | ≥84 | ≥99 | ≥99 | ≥99 | |
| ZrO₂ | – | – | – | – | ≥11 | – | – | – | |
| غير ذلك | ≤3.0 | ≤3.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤1.0 | ≤1.0 | ≤1.0 | |
| Standard size（L*W*T）mm | 1200/600*1000*(6-105),1200*500*(6-105) | 1000/900*600*20-150 | |||||||
| Package | Cartons or Pallets | Wooden | |||||||
| Other sizes of products and packages are available as required. | |||||||||
| Recommended using temperature:In oxidizing or neutral atmosphere,100~250℃Recommended usingtemperature:In oxidizing or neutral atmosphere,100∽250℃lower than the maximum service temperature,In reductive atmosphere,200~350℃ lower than the maximum service temperature. | |||||||||
التطبيقات
- جلدة الإحكام عالية الحرارة
- أجزاء مقاومة للتآكل في تطبيقات داخل البطانة
- مادة سطح ساخنة لبطانة أفران درجات الحرارة العالية
- عزل حراري لأجهزة التسخين
- مادة تعبئة لباب الفرن والجسم